Elemental partitioning effects because of crystal progress procedures in binary NiAl alloys are uncovered. The directional solidification approach is analysed in terms of a solidification design of binary NiAl alloys possessing regard into a composition dependent partition coefficient. The predictions are as opposed with electron probe microa